Local mechanical properties of intercritically reheated coarse grained heat affected zone in low alloy steel

Bidragsytere:
  • Veronica Gausel Haugen
  • Bjørn Rune Sørås Rogne
  • Odd Magne Akselsen
  • Christian Thaulow og
  • Erling Østby

Tidsskrift

Materials & Design
ISSN 0261-3069
NVI-nivå 0

Om resultatet

Vitenskapelig artikkel
Publiseringsår: 2014
Publisert online: 2014
Trykket: 2014
Volum: 59
Sider: 135 - 140

Importkilder

Scopus-ID: 2-s2.0-84896310222

Beskrivelse Beskrivelse

Tittel

Local mechanical properties of intercritically reheated coarse grained heat affected zone in low alloy steel

Sammendrag

Steels applied in arctic climates are subjected to low temperature. Since they undergo ductile–brittle transition with falling temperature, their fracture toughness must be addressed, particularly after welding. To predict their behaviour requires knowledge on local properties. Thus, the present study concerns nanomechanical testing of typical microstructures present in the intercritically reheated coarse grained heat affected zone of a 490 MPa forging. Such microstructures were achieved by weld thermal simulation of samples with 11 mm × 11 mm cross section and 100 mm length, using peak temperature of 1350 °C in the first cycle and 780 °C in the second cycle. Both cycles used cooling time Δt8/5 of 5 or 10 s. This caused formation of M–A phases along prior austenite grain boundaries and mixture of bainite/tempered martensite in the bulk. Nanomechanical testing was performed by compression of nanopillars prepared in grain boundary located M–A phases and in the bulk of the grains. The results achieved showed significant that the grain boundary phase possesses much higher strength than the grain bulk. It is also shown that there is large scatter in the stress–strain data, depending on the actual local microstructure being tested.

Bidragsytere

Veronica Gausel Haugen

  • Tilknyttet:
    Forfatter
    ved Institutt for maskinteknikk og produksjon ved Norges teknisk-naturvitenskapelige universitet

Bjørn Rune Sørås Rogne

  • Tilknyttet:
    Forfatter
    ved Institutt for maskinteknikk og produksjon ved Norges teknisk-naturvitenskapelige universitet

Odd Magne Akselsen

  • Tilknyttet:
    Forfatter
    ved Institutt for maskinteknikk og produksjon ved Norges teknisk-naturvitenskapelige universitet
  • Tilknyttet:
    Forfatter
    ved Materialer og nanoteknologi ved SINTEF AS

Christian Thaulow

  • Tilknyttet:
    Forfatter
    ved Institutt for maskinteknikk og produksjon ved Norges teknisk-naturvitenskapelige universitet

Erling Østby

  • Tilknyttet:
    Forfatter
    ved Materialer og nanoteknologi ved SINTEF AS
1 - 5 av 5