Improving thermal stability in Cu-containing Al-Mg-Si alloys by precipitate optimization

Bidragsytere:
  • Calin Daniel Marioara
  • Sigmund Jarle Andersen
  • Jostein Røyset
  • Oddvin Reiso
  • Sverre Gulbrandsen-Dahl
  • Tor-Erik Nicolaisen
  • mfl.

Tidsskrift

Metallurgical and Materials Transactions A
ISSN 1073-5623
e-ISSN 1543-1940
NVI-nivå 2

Om resultatet

Vitenskapelig artikkel
Publiseringsår: 2014
Publisert online: 2014
Trykket: 2014
Volum: 45
Hefte: 7
Sider: 2938 - 2949

Importkilder

Scopus-ID: 2-s2.0-84899911715

Beskrivelse Beskrivelse

Tittel

Improving thermal stability in Cu-containing Al-Mg-Si alloys by precipitate optimization

Sammendrag

It is demonstrated that good thermal stability in Al-Mg-Si-Cu aluminum alloys correlates with a high density of fine lath-shaped, Cu-containing, disordered L-precipitates. Alloys optimized for L retained hardness above 90 HV after 3 weeks over-aging at 473 K (200 °C). Further improvement was achieved by substituting Si by Ge in one alloy. High-angle annular dark-field scanning transmission electron microscopy showed that at peak-hardness conditions, L coexists with more common needle-shaped precipitates, often with Cu-enriched interfaces.

Bidragsytere

Calin Daniel Marioara

  • Tilknyttet:
    Forfatter
    ved Materialer og nanoteknologi ved SINTEF AS

Sigmund Jarle Andersen

  • Tilknyttet:
    Forfatter
    ved Materialer og nanoteknologi ved SINTEF AS

Jostein Røyset

  • Tilknyttet:
    Forfatter
    ved Norsk Hydro ASA

Oddvin Reiso

  • Tilknyttet:
    Forfatter
    ved Norsk Hydro ASA

Sverre Gulbrandsen-Dahl

  • Tilknyttet:
    Forfatter
    ved SINTEF Manufacturing
  • Tilknyttet:
    Forfatter
    ved Institutt for materialteknologi ved Norges teknisk-naturvitenskapelige universitet
1 - 5 av 9 | Neste | Siste »