Aging of polyamide 11. Part 1: Evaluating degradation by thermal, mechanical, and viscometric analysis

Bidragsytere:
  • Tobiasz Mazan
  • Randi Berggren
  • Jens Kjær Jørgensen og
  • Andreas Echtermeyer

Tidsskrift

Journal of Applied Polymer Science
ISSN 0021-8995
e-ISSN 1097-4628
NVI-nivå 1

Om resultatet

Vitenskapelig artikkel
Publiseringsår: 2015
Volum: 132
Hefte: 20
Artikkelnummer: 41971

Importkilder

Scopus-ID: 2-s2.0-84923559223

Beskrivelse Beskrivelse

Tittel

Aging of polyamide 11. Part 1: Evaluating degradation by thermal, mechanical, and viscometric analysis

Sammendrag

Hydrolytic degradation at elevated temperatures is a key reason for failure in offshore flexible risers. In this article, the aging of polyamide 11 in deoxygenated water at 90°C and 120°C was studied. Tensile and dynamic mechanical thermal analysis tests were performed to measure changes in mechanical properties. Viscometry, gravimetric measurements, differential scanning calorimetry, and thermogravimetric analysis were used to link these properties with morphological changes. General trends are increased stiffness, tensile strength, and glass transition temperature as well as decreased glassy state damping efficiency with increased aging times. Changes can be initially ascribed to plasticizer depletion and then to interplay between molecular weight decrease and crystallinity increase. Viscosity at hydrolysis equilibrium indicates that brittle failure typically involves oxidation or UV exposure.

Bidragsytere

Tobiasz Mazan

  • Tilknyttet:
    Forfatter
    ved Institutt for maskinteknikk og produksjon ved Norges teknisk-naturvitenskapelige universitet

Randi Berggren

  • Tilknyttet:
    Forfatter
    ved Institutt for maskinteknikk og produksjon ved Norges teknisk-naturvitenskapelige universitet

Jens Kjær Jørgensen

  • Tilknyttet:
    Forfatter
    ved Materialer og nanoteknologi ved SINTEF AS

Andreas Echtermeyer

  • Tilknyttet:
    Forfatter
    ved Institutt for maskinteknikk og produksjon ved Norges teknisk-naturvitenskapelige universitet
1 - 4 av 4