Tailored porosities of the cathode layer for improved polymer electrolyte fuel cell performance

Bidragsytere:
  • Agnieszka Zlotorowicz
  • Kaushik Jayasayee
  • Paul Inge Dahl
  • Magnus Skinlo Thomassen og
  • Signe Kjelstrup

Tidsskrift

Journal of Power Sources
ISSN 0378-7753
e-ISSN 1873-2755
NVI-nivå 1

Om resultatet

Vitenskapelig artikkel
Publiseringsår: 2015
Publisert online: 2015
Trykket: 2015
Volum: 287
Sider: 472 - 477
Artikkelnummer: 2015.04.07
Open Access

Importkilder

Scopus-ID: 2-s2.0-84929086264

Beskrivelse Beskrivelse

Tittel

Tailored porosities of the cathode layer for improved polymer electrolyte fuel cell performance

Sammendrag

We show experimentally for the first time that the introduction of macro-pores in the nanoporous catalyst layer of a polymer electrolyte membrane fuel cell can improve its performance. We have achieved a Pt utilization of about 0.23 mg W−1 at 0.6 V which is twice the value of the DOE target for 2020, and three times (0.60 mg W−1) smaller than the value of a fully nanoporous reference layer at a catalyst loading of 0.11 mg cm−2. In this work, monodispersed polystyrene particles with diameters of 0.5 and 1 μm were used as pore formers. Cathode catalyst layers with macroporous volume fractions between 0 and 0.58 were investigated. Maximum performance was observed for fuel cells with a macroporous volume fraction of about 0.52 for a 1 μm thick catalyst layer. The results, which were obtained for the cathode layer, support earlier theoretical predictions that gas access to and water escape from the catalyst can be facilitated by introduction of macropores in the nanoporous layer.

Bidragsytere

Agnieszka Zlotorowicz

  • Tilknyttet:
    Forfatter
    ved Institutt for kjemi ved Norges teknisk-naturvitenskapelige universitet

Kaushik Jayasayee

  • Tilknyttet:
    Forfatter
    ved Bærekraftig energiteknologi ved SINTEF AS

Paul Inge Dahl

  • Tilknyttet:
    Forfatter
    ved Bærekraftig energiteknologi ved SINTEF AS

Magnus Thomassen

Bidragsyterens navn vises på dette resultatet som Magnus Skinlo Thomassen
  • Tilknyttet:
    Forfatter
    ved Bærekraftig energiteknologi ved SINTEF AS
Aktiv cristin-person

Signe Helene Kjelstrup

Bidragsyterens navn vises på dette resultatet som Signe Kjelstrup
  • Tilknyttet:
    Forfatter
    ved Institutt for kjemi ved Norges teknisk-naturvitenskapelige universitet
1 - 5 av 5