Al-doped ZnO prepared by co-precipitation method and its thermoelectric characteristics

Bidragsytere:
  • Jeyanthinath Mayandi
  • Reshma Krishnan Madathil
  • C Abinaya
  • Kevin Bethke
  • Vishnukanthan Venkatachalapathy
  • Klaus Rademann
  • mfl.

Tidsskrift

Materials Letters
ISSN 0167-577X
e-ISSN 1873-4979
NVI-nivå 1

Om resultatet

Vitenskapelig artikkel
Publiseringsår: 2021
Volum: 288
Artikkelnummer: 129352

Importkilder

Scopus-ID: 2-s2.0-85100290193

Beskrivelse Beskrivelse

Tittel

Al-doped ZnO prepared by co-precipitation method and its thermoelectric characteristics

Sammendrag

We report on structural and electrical characterization of zinc oxide material containing aluminum (Al:ZnO) prepared by a co-precipitation technique using different zinc and aluminum precursors. The as-prepared powders were calcinated and pre-annealed at 600 °C and 1200 °C. These were cold-pressed to pellets and sintered at 1000 °C. We also prepared ZnO material with no Al for comparisons. The electrical and thermal conductivity, as well as the Seebeck coefficient, were measured. These properties were correlated with structural analysis by X-ray diffraction characterization and scanning electron microscopy. The process yields a nanostructured material with much reduced thermal conductivity.

Bidragsytere

Jeyanthinath Mayandi

  • Tilknyttet:
    Forfatter
    ved Senter for materialvitenskap og nanoteknologi ved Universitetet i Oslo
  • Tilknyttet:
    Forfatter
    ved Madurai Kamaraj University

Reshma Krishnan Madathil

  • Tilknyttet:
    Forfatter
    ved Senter for Materialvitenskap og Nanoteknologi kjemi ved Universitetet i Oslo
  • Tilknyttet:
    Forfatter
    ved Kjemisk institutt ved Universitetet i Oslo

C Abinaya

  • Tilknyttet:
    Forfatter
    ved Madurai Kamaraj University

Kevin Bethke

  • Tilknyttet:
    Forfatter
    ved Humboldt-Universität zu Berlin

Vishnukanthan Venkatachalapathy

  • Tilknyttet:
    Forfatter
    ved National Research Nuclear University "MEPHI"
  • Tilknyttet:
    Forfatter
    ved Senter for materialvitenskap og nanoteknologi ved Universitetet i Oslo
1 - 5 av 8 | Neste | Siste »