Thermal transport in silver-coated polymer sphere composites by the bidirectional 3ω method

Bidragsytere:
  • Susanne Sandell
  • Thorstein Wang
  • Emigdio Chavez-Angel
  • Helge Kristiansen
  • Zhiliang Zhang og
  • Jianying He

Tidsskrift

Journal of Applied Physics
ISSN 0021-8979
e-ISSN 1089-7550
NVI-nivå 1

Om resultatet

Vitenskapelig artikkel
Publiseringsår: 2022
Volum: 131
Hefte: 12
Artikkelnummer: 125107

Importkilder

Scopus-ID: 2-s2.0-85127990017

Beskrivelse Beskrivelse

Tittel

Thermal transport in silver-coated polymer sphere composites by the bidirectional 3ω method

Sammendrag

The bidirectional 3ω method is an electrothermal technique that is commonly used to obtain the thermal conductivity of materials such as liquids, biological samples and pastes. In this work, an epoxy-based adhesive was filled with monodisperse 10 μm polymethyl methacrylate (PMMA) spheres coated with silver thin films (AgPS), such that a metallic network that dominated the thermal transport was formed through the composite. The bidirectional 3Ω method was used to obtain the thermal conductivity of the conductive adhesive at different volume fractions of AgPS. For 50 vol.% AgPS, corresponding to 3.4 vol.% silver, the thermal conductivity was 2.03 ± 0.21 W/m-1K-1. The results show that the thermal conductivity is strongly correlated with the AgPS volume fraction, while maintaining a volume fraction of silver far below commercial silver paste, which has typical filler fractions of 40 vol.\% silver. The results of this work were compared to thermal measurements of the same material by other techniques, and advantages and disadvantages of the methods were finally discussed.

Bidragsytere

Susanne Sandell

  • Tilknyttet:
    Forfatter
    ved Institutt for konstruksjonsteknikk ved Norges teknisk-naturvitenskapelige universitet

Thorstein Wang

  • Tilknyttet:
    Forfatter
    ved Institutt for konstruksjonsteknikk ved Norges teknisk-naturvitenskapelige universitet

Emigdio Chavez-Angel

  • Tilknyttet:
    Forfatter
    ved Institut Català de Nanociència i Nanotecnologia

Helge Kristiansen

  • Tilknyttet:
    Forfatter
    ved Conpart AS
  • Tilknyttet:
    Forfatter
    ved Institutt for konstruksjonsteknikk ved Norges teknisk-naturvitenskapelige universitet

Zhiliang Zhang

  • Tilknyttet:
    Forfatter
    ved Institutt for konstruksjonsteknikk ved Norges teknisk-naturvitenskapelige universitet
1 - 5 av 6 | Neste | Siste »