Investigation of Two Immiscible Liquids Wetting at Elevated Temperature: Interaction Between Liquid FeMn Alloy and Liquid Slag

Bidragsytere:
  • Sarina Bao
  • Merete Tangstad
  • Kai Tang
  • Kristian Etienne Einarsrud
  • Martin Syvertsen
  • Morten Ingar Onsøien
  • mfl.

Tidsskrift

Metallurgical and Materials Transactions B
ISSN 1073-5615
e-ISSN 1543-1916
NVI-nivå 2

Om resultatet

Vitenskapelig artikkel
Publiseringsår: 2021
Publisert online: 2021

Importkilder

Scopus-ID: 2-s2.0-85107729772

Beskrivelse Beskrivelse

Tittel

Investigation of Two Immiscible Liquids Wetting at Elevated Temperature: Interaction Between Liquid FeMn Alloy and Liquid Slag

Sammendrag

The goal of the current work is to develop a methodology to study the wetting behaviour of two immiscible liquids at high temperatures, and to investigate the parameters which influence the wetting properties. The wetting behaviour between synthetic FeMn alloy and synthetic slag has been investigated using the sessile drop technique. Two experimental procedures were implemented under both Ar and CO atmospheres: (a) FeMn alloy and slag placed next to each other on a graphite substrate; and (b) one droplet dropped on top of the other. FactSage is applied to calculate reactions and their equilibrium. The current work presents and demonstrates the suggested methodologies. The results indicate that the wetting between slag and FeMn alloy is relatively stable at temperatures up to 100 K above their melting points, regardless of the droplet size and atmosphere. MnO reduction is accelerated at higher temperature, especially in CO, thus increasing the wetting between FeMn alloy and slag, eventually fusing together. At even higher temperature, slag separates from FeMn alloy due to changing chemical composition during non-equilibrium MnO reduction.

Bidragsytere

Aktiv cristin-person

Sarina Bao

  • Tilknyttet:
    Forfatter
    ved Metallproduksjon og prosessering ved SINTEF AS

Merete Tangstad

  • Tilknyttet:
    Forfatter
    ved Institutt for materialteknologi ved Norges teknisk-naturvitenskapelige universitet

Kai Tang

  • Tilknyttet:
    Forfatter
    ved Metallproduksjon og prosessering ved SINTEF AS

Kristian Etienne Einarsrud

  • Tilknyttet:
    Forfatter
    ved Institutt for materialteknologi ved Norges teknisk-naturvitenskapelige universitet

Martin Syvertsen

  • Tilknyttet:
    Forfatter
    ved Metallproduksjon og prosessering ved SINTEF AS
1 - 5 av 8 | Neste | Siste »