A Study of Bubble Behavior and Anode Effect on the Graphite and Industrial Carbon Anode in a See-Through Furnace During Aluminium Electrolysis

Anode gas bubble behavior and anode effect on graphite and industrial carbon rod-shaped anode in a cryolite melt have been studied using a see-through furnace. The different carbon materials have different properties which can affect bubble behavior and electrochemical properties. Industrial carbon is more inhomogeneous with respect to structure, pore, aggregates and impurities in comparison to the graphite. More bubbles were nucleated on the industrial carbon than on the graphite for the same current density. The time related to the coalescence process for both anodes was found to be in interval 16 to 24 ms and independent of the current densities. Bubbles detached from the horizontal surface of the anode have similar average diameter value for both anodes for current densities 1.0 A cm−2, the average diameter is lower for the industrial carbon anode. The onset of the anode effect occurred faster on the graphite than on the industrial anode. The PFC-containing gas layer appeared to be thicker and more stable on the graphite anode than on the industrial carbon anode.